This is a perfect shrink film. It can help you solve nearly all shrinking difficulties. JT06 has excellent low shrink temperature property. Its shrink temperature is nearly same as PVC shrink film's. With quick shrink, good seal strength and over 70% shrinkage, JT06 can perform perfectly even under the worst shrink conditions. JT06 also has low shrink force function and good hot slip property.
TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUES | ||||
---|---|---|---|---|---|---|---|
THICKNESS | 12um | 15um | 19um | 25um | |||
TENSILE | |||||||
Tensile Strength (MD) | N/mm2 | D882 | 76 | 76 | 69 | 66 | |
Tensile Strength (TD) | 66 | 66 | 64 | 59 | |||
Elongation (MD) | % | 96 | 101 | 94 | 91 | ||
Elongation (TD) | 86 | 94 | 86 | 79 | |||
TEAR | |||||||
MD | g | D1922 | 14.6 | 16.6 | 24.1 | 30.6 | |
TD | 15.1 | 16.1 | 23.1 | 32.1 | |||
SEAL STRENGTH | |||||||
MD/Hot Wire Seal | N/mm | F88 | 0.78 | 0.85 | 1.05 | 1.45 | |
TD/Hot Wire Seal | 0.75 | 0.82 | 1.01 | 1.35 | |||
COF(film to Film) | |||||||
Dynamic | D1894 | 0.31 | 0.27 | 0.26 | 0.32 | ||
Static | 0.32 | 0.29 | 0.28 | 0.33 | |||
Static (Hot Slip) @ 60℃ | 0.41 | 0.38 | 0.36 | 0.34 | |||
OPTICS | |||||||
Haze | D1003 | 3.6 | 4.0 | 4.4 | 4.6 | ||
Clarity | D1746 | 97.6 | 98.1 | 97.0 | 95.1 | ||
Gloss @ 45Deg | D2457 | 82.1 | 84.1 | 84.0 | 80.6 | ||
BARRIER | |||||||
Oxygen Transmission Rate | cc/m2/day | D3985 | 12900 | 11700 | 9600 | 6500 | |
Water Vapor Transmission Rate | gm/m2/day | F1249 | 53 | 46 | 39 | 32 | |
SHRINKAGE PROPERTIES | MD | TD | MD | TD | |||
Free Shrinkage | 80℃ | % | D2732 | 18 | 21 | 16 | 18 |
90℃ | 26 | 33 | 23 | 29 | |||
100℃ | 44 | 48 | 43 | 48 | |||
110℃ | 56 | 57 | 55 | 56 | |||
120℃ | 64 | 65 | 63 | 63 | |||
130℃ | 69 | 68 | 68 | 66 | |||
Shrink Tension | 90℃ | Mpa | D2838 | 2.00 | 2.30 | 2.05 | 2.20 |
100℃ | 2.35 | 2.50 | 2.50 | 2.60 | |||
110℃ | 2.65 | 2.75 | 2.85 | 2.95 | |||
120℃ | 2.55 | 2.60 | 2.70 | 2.70 |